TEROSON PU 9097 PL HLMC SET

Teroson PU 9097 PL HMLC SET is a 1 component moisture curing polyurethane adhesive.

• 
  
• Excellent adhesion without primer to glass, ceramic coated glass and on painted surfaces
  
• High eleasticity and shear modulus
  
• Very low conductivity
  
• Good adhesion to primer
  
• Good adhesion to material residues and PUR pre-coatings
  
• High curing rate
  
• High UV resistance without primer
  
• High shear strength, retained on ageing
  

• 
  
• Colour : black
  
• Odour : weak
  
• Consistency : sag-resistant paste
  
• Density : approx. 1.3 g/cm3
  
• Solids : 100%
  
• Curing mechanism : moisture curing
  
• Cure rate (DIN 50014 standard climate: 23°C, 50% rh) : approx. 3-4 mm/24 h
  
• Shore-A-hardness (DIN 53505) : approx. 66
  
• Tensile strength (DIN 53504) : approx. 8.0 MPa
  
• Stress (DIN 53504): approx. 3.5 MPa at 100 % elongation
  
• Shear modulus (based on DIN 54451) : approx. 2.7 MPa
  
• Elongation at break (DIN 53504) : approx. 280 %
  
• Shear strength (thickness 5 mm, based on DIN EN 1465) : 1.8 MPa (after 24 h DIN 50014)
  
  5.5 MPa (fully cured)
  
• Volume change (DIN 52451) : < 1 %
  
• Glazing time : maximum 25 min. * standard climate
  
• Application temperature : +10°C to +35°C
  
• In service temperature range : -40°C to +90°C
  
  short exposure (up to 1 h) : +120°C