TEROSON PU 8599 HMLC SET IN KIT

TEROSON PU 8599 HLMC SET

Teroson PU 8599 HMLC is a 1-component polyurethane adhesive with high shear modulus and low conductivity.

• 
  
• Very good sag resistance
  
• High cure rate
  
• High elastic and shear strength, even after aging
  
• Good adhesion to the remaining material
  
• Excellent adhesion to glass, glass with the ceramic coating,encapsulation and to painted surfaces, in connection withprimer/activator
  
• High UV resistance in connection with primer/activator
  
• High shear modulus
  
• Extremely high position tack
  

• 
  
• Colour : black
  
• Odour : weak
  
• Consistency : smooth, sag-resistant, pasty
  
• Density : approx. 1.25 g/cm3
  
• Solids : 100%
  
• Curing mechanism : humidity curing
  
• Cure rate (DIN 50014 ; 23°C, 50% rh) : approx. 3 to 4 mm/24 hrs
  
• Shore-A-hardness (DIN 53505): approx. 75
  
• Tensile strength (DIN 53504): approx. 10.5 MPa
  
• Stress (DIN 53504): approx. 6 MPa at 100 % elongation
  
• Shear modulus (DIN 54451): approx. 3.2 MPa
  
• Elongation at break (DIN 53504): approx. 350 %
  
• Shear strength
  
  after 24h (DIN 54451) : 1.8 MPa
  
  Layer thickness 5 mm based on DIN 54451 : 4 to 5 MPa (fully cured)
  
• Specific forward resistance (ASTM D 257-99 / DIN IEC 60093) : approx. 1×1010 ω cm
  
• Volume change (DIN 52451) : < 1 %
  
• Glazing time* : approx. 15 mins
  
• Material application temperature : +60°C to +70°C
  
• Environmental temperature at application : -10°C to +45°C
  
• In service temperature range : -40°C to +90°C
  
  short exposure (up to 1 hr.) : +120°C