TEROSON PU 8630 HLMC SET IN KIT

TEROSON PU 8630 HLMC SET

Teroson PU 8630 HMLC SET is a bi-component polyurethane adhesive with high shear modulus and low conductivity.

• 
  
• Very good sag resistance
  
• High elastic and shear strength, even after aging
  
• Very low conductivity
  
• Good adhesion to the remaining material
  
• Excellent adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces, in connection with primer/activator
  
• High UV resistance in connection with primer/activator
  
• High shear modulus
  
• Easy to use ( application with battery gun / 1C pneumatic gun)
  

• 
  
• Colour : black
  
• Odour : weak
  
• Consistency : smooth, sag-resistant, pasty
  
• Density : approx. 1.2 g/cm3
  
• Solids : 100%
  
• Shore-A-hardness (DIN 53505): approx. 60
  
• Tensile strength (DIN 53504): approx. 9.5 MPa
  
• Stress (DIN 53504): approx. 5.7 MPa at 100 % elongation
  
• Shear modulus (DIN 54451): approx. 3.0 MPa
  
• Elongation to break (DIN 53504): approx. 370 %
  
• Shear strength (thickness 5mm, 5–6 MPa (fully cured) based on DIN EN 1465) :
  
  approx. 4 to 5 MPa (fully cured)
  
• Specific forward resistance (ASTM D 257-99 / DIN IEC 60093) : approx. 1×1010 ω cm
  
• Volume change (DIN 52451) : < 1 %
  
• Glazing time* : max. 25 mins
  
• Material application temperature : +60°C to +70°C
  
• In service temperature range : -40°C to +90°C
  
  short exposure (up to 1 hr.) : +120°C