TEROSON PU 8596 SET IN KIT

TEROSON PU 8596 SET

Teroson PU 8596 is a one-component, moisture curing Direct Glazing Sealant with excellent sag resistance based on polyurethane.

• 
  
• Cures by reaction with moisture to a soft elastic product
  
• The skin formation and curing times are dependent on humidity and temperature
  
• The curing time also depends on joint depth
  
• By increasing the temperature and moisture these times can be reduced
  
• Low temperature as well as low moisture retard the process
  

• 
  
• excellent adhesion with Primer Terostat-8517 H on glass, ceramic coated glass and on painted surfaces
  
• excellent adhesion on material residues
  
• high cure rate
  
• high UV resistance in connection with Primer Terostat-8517 H
  
• high shear strength, retained on ageing.
  

• 
  
• Colour : black
  
• Odour : weak
  
• Consistency : smooth, sag-resistant paste
  
• Density : approx. 1.2 g/cm3
  
• Solids : 100%
  
• Cure rate: approx. 5 mm/24 h
  
  (DIN 50014 standard climate: 23°C, 50 % rh)
  
• Shore-A-hardness (DIN 53505): approx. 55
  
• Tensile strength (DIN 53504): approx. 8.5 MPa
  
• Stress (DIN 53504): approx. 2.5 MPa at 100 % elongation
  
• Shear modulus (DIN 54451): approx. 1.2 MPa
  
• Elongation to break (DIN 53504): approx. 300 %
  
• Shear strength (thickness 5mm, 5–6 MPa (fully cured) based on DIN EN 1465) : approx. 2 MPa (after 24 h DIN 50014)
  
• Volume change (DIN 52451): < 1 %
  
• Glazing time: maximum 25 mins *
  
• Application temperature: 5°C to 35°C
  
• In service temperature range: -40°C to 90°C
  
  short exposure (up to 1 hr.): 120°C